| Pore Volume | 0.6-0.8 Cm3/g |
|---|---|
| Na2O Content | ≤0.2% |
| Surface Area | 100-110 M2/g |
| Mgo Content | ≤0.05% |
| Thermal Stability | Up To 1200℃ |
| Application | Catalyst For Dehydrogenation Of Long Chain Alkanes |
|---|---|
| Surface Area | 150-170 M2/g |
| Pore Size | 10-15nm |
| Pore Volume | 0.8-1.2 Cm3/g |
| Bulk Density | 0.3-0.4 G/cm3 |
| Moisture Content | Less Than 1% |
|---|---|
| Application | Catalyst For Dehydrogenation Of Long Chain Alkanes |
| Surface Area | 150-170 M2/g |
| Catalytic Activity | High Selectivity And Conversion Rate |
| Pore Size | 10-15nm |
| Thermal Stability | Up To 1000°C |
|---|---|
| Thermal Conductivity | High |
| Shape | Sphere |
| Bulk Density | 0.55-0.66 G/cm3 |
| Electrical Insulation | Excellent |
| Pore Size | Medium |
|---|---|
| Thermal Stability | Up To 1000°C |
| Shape | Sphere |
| Crush Strength | 50 Lbs |
| Surface Area | 200 M2/g |
| Abrasion Resistance | Excellent |
|---|---|
| Material | Alumina |
| Mechanical Strength | High |
| Water Absorption | Low |
| Surface Area | 200 M2/g |
| Material | Alumina |
|---|---|
| Electrical Insulation | Excellent |
| Abrasion Resistance | Excellent |
| Water Absorption | Low |
| Thermal Stability | Up To 1000°C |
| Carrier Material | Alumina |
|---|---|
| Boiling Point | Not Available |
| Specific Surface Area | ≥850 M2/g |
| Storage | Store In Dry Place |
| Particle Size | 2.2-2.6mm |
| Na2O Content | ≤0.2% |
|---|---|
| Cao Content | ≤0.05% |
| Moisture Content | ≤1% |
| Appearance | White Powder |
| Sio2 Content | ≤0.05% |
| Cao Content | ≤0.05% |
|---|---|
| Sio2 Content | ≤0.05% |
| Particle Size | 1.6-1.8mm |
| Na2O Content | ≤0.2% |
| Bulk Density | 0.6-0.65 G/cm3 |