Description | The PDH Alumina Carrier Is A High-performance Material Known For Its Unique Characteristics And Vital Role In Catalytic Processes. |
---|---|
Chemical Stability | Acid And Alkali Resistant |
Bulk Density | 0.6-0.65 G/cm3 |
Pore Size | 0.4-0.6nm |
Applications | Essential For The Dehydrogenation Of Propane, A Key Process In Producing Propylene Within The Petrochemical Sector. |
Abrasion Resistance | Excellent |
---|---|
Chemical Resistance | Acids And Bases |
Material | Alumina |
Thermal Conductivity | High |
Pore Size | Medium |
Material | Alumina |
---|---|
Electrical Insulation | Excellent |
Abrasion Resistance | Excellent |
Water Absorption | Low |
Thermal Stability | Up To 1000°C |
Abrasion Resistance | Excellent |
---|---|
Material | Alumina |
Mechanical Strength | High |
Water Absorption | Low |
Surface Area | 200 M2/g |
Pore Size | Medium |
---|---|
Thermal Stability | Up To 1000°C |
Shape | Sphere |
Crush Strength | 50 Lbs |
Surface Area | 200 M2/g |
Water Absorption | Low |
---|---|
Thermal Conductivity | High |
Shape | Sphere |
Crush Strength | 50 Lbs |
Surface Area | 200 M2/g |
Surface Area | 100-110 M2/g |
---|---|
Cao Content | ≤0.05% |
Bulk Density | 0.6-0.65 G/cm3 |
Sio2 Content | ≤0.05% |
Chemical Formula | Al2O3 |
Thermal Stability | Up To 1000°C |
---|---|
Thermal Conductivity | High |
Shape | Sphere |
Bulk Density | 0.55-0.66 G/cm3 |
Electrical Insulation | Excellent |
Crystalline Phase | Q-Al2O3 |
---|---|
Fe2O3 Content | ≤0.02% |
Particle Size | 1.6-1.8mm |
Pore Volume | 0.6-0.8 Cm3/g |
Moisture Content | ≤1% |
Cao Content | ≤0.05% |
---|---|
Sio2 Content | ≤0.05% |
Particle Size | 1.6-1.8mm |
Na2O Content | ≤0.2% |
Bulk Density | 0.6-0.65 G/cm3 |