Mgo Content | ≤0.05% |
---|---|
Particle Size | 1.6-1.8mm |
Appearance | White Powder |
Surface Area | 100-110 M2/g |
Cao Content | ≤0.05% |
Pore Volume | 0.6-0.8 Cm3/g |
---|---|
Na2O Content | ≤0.2% |
Surface Area | 100-110 M2/g |
Crystalline Phase | Q-Al2O3 |
Moisture Content | ≤1% |
Application | Catalyst For Dehydrogenation Of Long Chain Alkanes |
---|---|
Bulk Density | 0.3-0.4 G/cm3 |
Surface Area | 150-170 M2/g |
Pore Size | 10-15nm |
Alumina Content | More Than 99% |
Appearance | White Powder |
---|---|
Na2O Content | ≤0.2% |
Bulk Density | 0.6-0.65 G/cm3 |
Chemical Formula | Al2O3 |
Mgo Content | ≤0.05% |
Reaction Selectivity | 95-98% |
---|---|
Pore Size | 0.3-0.5 Nm |
Catalyst Life | 2-3 Years |
Composition | Nickel, Cobalt, Molybdenum, Alumina |
Bulk Density | 0.7-0.9 G/cm3 |
Mgo Content | ≤0.05% |
---|---|
Packing Density | 0.7-0.9g/cm3 |
Pore Size | 0.4-0.6nm |
Temperature Resistance | High Temperature Resistance |
Chemical Stability | Acid And Alkali Resistant |
Water Absorption | Low |
---|---|
Thermal Conductivity | High |
Chemical Resistance | Acids And Bases |
Thermal Stability | Up To 1000°C |
Material | Alumina |
Shape | Sphere |
---|---|
Bulk Density | 0.55-0.66 G/cm3 |
Electrical Insulation | Excellent |
Thermal Conductivity | High |
Water Absorption | Low |
Thermal Conductivity | High |
---|---|
Shape | Sphere |
Thermal Stability | Up To 1000°C |
Chemical Resistance | Acids And Bases |
Surface Area | 200 M2/g |
Size | 1/8 Inch |
---|---|
Shape | Sphere |
Mechanical Strength | High |
Abrasion Resistance | Excellent |
Thermal Stability | Up To 1000°C |