| Mgo Content | ≤0.05% |
|---|---|
| Particle Size | 1.6-1.8mm |
| Appearance | White Powder |
| Surface Area | 100-110 M2/g |
| Cao Content | ≤0.05% |
| Storage | Store In Dry Place |
|---|---|
| Particle Size | 2.2-2.6mm |
| Solubility | Insoluble In Water |
| Carrier Material | Alumina |
| Purity | ≥99% |
| Storage | Store In Dry Place |
|---|---|
| Application | Catalyst For 2-ethylanthraquinone Hydrogenation |
| Specific Surface Area | ≥850 M2/g |
| Solubility | Insoluble In Water |
| Particle Size | 2.2-2.6mm |
| Crush Strength | 50 Lbs |
|---|---|
| Material | Alumina |
| Surface Area | 200 M2/g |
| Thermal Conductivity | High |
| Mechanical Strength | High |
| Particle Size | 2.2-2.6mm |
|---|---|
| Specific Surface Area | ≥850 M2/g |
| Solubility | Insoluble In Water |
| Application | Catalyst For 2-ethylanthraquinone Hydrogenation |
| Storage | Store In Dry Place |
| Bulk Density | 0.6-0.65 G/cm3 |
|---|---|
| Mgo Content | ≤0.05% |
| Sio2 Content | ≤0.05% |
| Fe2O3 Content | ≤0.02% |
| Thermal Stability | Up To 1200℃ |
| Surface Area | 100-110 M2/g |
|---|---|
| Appearance | White Powder |
| Fe2O3 Content | ≤0.02% |
| Moisture Content | ≤1% |
| Bulk Density | 0.6-0.65 G/cm3 |
| Crystalline Phase | Q-Al2O3 |
|---|---|
| Moisture Content | ≤1% |
| Cao Content | ≤0.05% |
| Mgo Content | ≤0.05% |
| Surface Area | 100-110 M2/g |
| Storage | Store In Dry Place |
|---|---|
| Solubility | Insoluble In Water |
| Carrier Material | Alumina |
| Boiling Point | Not Available |
| Purity | ≥99% |
| Pore Size | 15-25nm |
|---|---|
| Shape | Spherical |
| Material | Alumina |
| Chemical Composition | Al2O3 |
| Regenerability | Good |