| Water Absorption | Low |
|---|---|
| Thermal Conductivity | High |
| Shape | Sphere |
| Crush Strength | 50 Lbs |
| Surface Area | 200 M2/g |
| Solubility | Insoluble In Water |
|---|---|
| Purity | ≥99% |
| Particle Size | 2.2-2.6mm |
| Carrier Material | Alumina |
| Specific Surface Area | ≥850 M2/g |
| Specific Surface Area | ≥850 M2/g |
|---|---|
| Particle Size | 2.2-2.6mm |
| Solubility | Insoluble In Water |
| Density | 0.54 G/cm3 |
| Boiling Point | Not Available |
| Crystalline Phase | Q-Al2O3 |
|---|---|
| Fe2O3 Content | ≤0.02% |
| Particle Size | 1.6-1.8mm |
| Pore Volume | 0.6-0.8 Cm3/g |
| Moisture Content | ≤1% |
| Solubility | Insoluble In Water |
|---|---|
| Particle Size | 2.2-2.6mm |
| Application | Catalyst For 2-ethylanthraquinone Hydrogenation |
| Density | 0.54 G/cm3 |
| Storage | Store In Dry Place |
| Fe2O3 Content | ≤0.02% |
|---|---|
| Bulk Density | 0.6-0.65 G/cm3 |
| Surface Area | 100-110 M2/g |
| Crystalline Phase | Q-Al2O3 |
| Moisture Content | ≤1% |
| Application | Catalyst For Dehydrogenation Of Long Chain Alkanes |
|---|---|
| Bulk Density | 0.3-0.4 G/cm3 |
| Surface Area | 150-170 M2/g |
| Pore Size | 10-15nm |
| Alumina Content | More Than 99% |
| Water Absorption | Low |
|---|---|
| Thermal Conductivity | High |
| Chemical Resistance | Acids And Bases |
| Thermal Stability | Up To 1000°C |
| Material | Alumina |
| Surface Area | 100-110 M2/g |
|---|---|
| Color | White |
| Cao Content | ≤0.05% |
| Particle Size | 1.6-1.8mm |
| Moisture Content | ≤1% |
| Fe2O3 Content | ≤0.02% |
|---|---|
| Mgo Content | ≤0.05% |
| Color | White |
| Na2O Content | ≤0.2% |
| Sio2 Content | ≤0.05% |