| Surface Area | 150-170 M2/g |
|---|---|
| Particle Size | 2 Mm |
| Pore Size | 10-15nm |
| Surface Hydroxyl Groups | High Concentration Of Surface Hydroxyl Groups |
| Application | Catalyst For Dehydrogenation Of Long Chain Alkanes |
| Application | Catalyst For 2-ethylanthraquinone Hydrogenation |
|---|---|
| Particle Size | 2.2-2.6mm |
| Solubility | Insoluble In Water |
| Density | 0.54 G/cm3 |
| Storage | Store In Dry Place |
| Boiling Point | Not Available |
|---|---|
| Density | 0.54 G/cm3 |
| Storage | Store In Dry Place |
| Specific Surface Area | ≥850 M2/g |
| Application | Catalyst For 2-ethylanthraquinone Hydrogenation |
| Particle Size | 2.2-2.6mm |
|---|---|
| Specific Surface Area | ≥850 M2/g |
| Purity | ≥99% |
| Carrier Material | Alumina |
| Boiling Point | Not Available |
| Bulk Density | 0.3-0.4 G/cm3 |
|---|---|
| Pore Size | 10-15nm |
| Alumina Content | More Than 99% |
| Catalytic Activity | High Selectivity And Conversion Rate |
| Moisture Content | Less Than 1% |
| Surface Hydroxyl Groups | High Concentration Of Surface Hydroxyl Groups |
|---|---|
| Surface Area | 150-170 M2/g |
| Application | Catalyst For Dehydrogenation Of Long Chain Alkanes |
| Moisture Content | Less Than 1% |
| Pore Size | 10-15nm |
| Particle Size | 2.2-2.6mm |
|---|---|
| Carrier Material | Alumina |
| Specific Surface Area | ≥850 M2/g |
| Storage | Store In Dry Place |
| Purity | ≥99% |
| Bulk Density | 0.3-0.4 G/cm3 |
|---|---|
| Surface Hydroxyl Groups | High Concentration Of Surface Hydroxyl Groups |
| Pore Volume | 0.8-1.2 Cm3/g |
| Catalytic Activity | High Selectivity And Conversion Rate |
| Pore Size | 10-15nm |
| Thermal Stability | Up To 1000°C |
|---|---|
| Surface Area | 150-170 M2/g |
| Pore Size | 10-15nm |
| Alumina Content | More Than 99% |
| Catalytic Activity | High Selectivity And Conversion Rate |
| Pore Volume | 0.6-0.8 Cm3/g |
|---|---|
| Particle Size | 1.6-1.8mm |
| Na2O Content | ≤0.2% |
| Fe2O3 Content | ≤0.02% |
| Crystalline Phase | Q-Al2O3 |