| Selectivity | 80% |
|---|---|
| Support Material | Alumina |
| Surface Area | 150-200 M2/g |
| Active Metal | Palladium |
| Application | Selective Hydrogenation Of C2 |
| Particle Size | 3-4.5 Mm |
|---|---|
| Support Material | Alumina |
| Shape | Spherical |
| Pressure | 3.5MPa |
| Industry | Chemical Industry |
| Surface Area | 150-200 M2/g |
|---|---|
| Application | Hydrogenation Of Cracked Gasoline |
| Shape | Spherical |
| Pore Size | 0.3-0.5 Nm |
| Composition | Nickel, Cobalt, Molybdenum, Alumina |
| Surface Area | 190-200 M2/g |
|---|---|
| Shape | Spherical |
| Size | 1.6-1.8 Mm |
| Pore Volume | 0.58-0.66 Cm3/g |
| Product Type | Solid Catalyst |
| Shape | Spherical |
|---|---|
| Heat Stability | High |
| Product Type | Solid Catalyst |
| Lifespan | 4-5 Years |
| Size | 1.6-1.8 Mm |
| Surface Area | 190-200 M2/g |
|---|---|
| Product Type | Solid Catalyst |
| Size | 1.6-1.8 Mm |
| Heat Stability | High |
| Lifespan | 4-5 Years |
| Shape | Spherical |
|---|---|
| Pore Volume | 0.58-0.66 Cm3/g |
| Lifespan | 4-5 Years |
| Size | 1.6-1.8 Mm |
| Heat Stability | High |
| Application | Propane Dehydrogenation (PDH) |
|---|---|
| Chemical Composition | Al2O3 ≥ 97% |
| Surface Area | 100-110m2/g |
| Thermal Stability | ≥900℃ |
| Surface Acidic Property | Strong |
| Temperature Range | 400-600 °C |
|---|---|
| Size | 1.6-1.8 Mm |
| Surface Area | ＞180 M2/g |
| Shape | Spherical |
| Bulk Density | 0.58-0.7 G/cm3 |
| Shape | Ball Or Bar |
|---|---|
| Material | Alumina |
| Chemical Composition | Al2O3 |
| Regenerability | Good |
| Application | Front-hydrogenation/post-hydrogenation |