Pore Size | Medium |
---|---|
Bulk Density | 0.55-0.66 G/cm3 |
Thermal Conductivity | High |
Chemical Resistance | Acids And Bases |
Thermal Stability | Up To 1000°C |
Mechanical Strength | High |
---|---|
Surface Area | 200 M2/g |
Water Absorption | Low |
Thermal Stability | Up To 1000°C |
Abrasion Resistance | Excellent |
Electrical Insulation | Excellent |
---|---|
Water Absorption | Low |
Size | 1/8 Inch |
Mechanical Strength | High |
Surface Area | 200 M2/g |
Application | Catalyst For 2-ethylanthraquinone Hydrogenation |
---|---|
Carrier Material | Alumina |
Storage | Store In Dry Place |
Particle Size | 2.2-2.6mm |
Specific Surface Area | ≥850 M2/g |
Particle Size | 1.6-1.8mm |
---|---|
Chemical Formula | Al2O3 |
Crystalline Phase | Q-Al2O3 |
Bulk Density | 0.6-0.65 G/cm3 |
Na2O Content | ≤0.2% |
Crystalline Phase | Q-Al2O3 |
---|---|
Chemical Formula | Al2O3 |
Particle Size | 1.6-1.8mm |
Cao Content | ≤0.05% |
Moisture Content | ≤1% |
Temperature Resistance | High Temperature Resistance |
---|---|
Chemical Stability | Acid And Alkali Resistant |
Purity | High Purity |
Specific Surface Area | ≥0.5m²/g |
Application | Catalyst Support |
Sio2 Content | ≤0.05% |
---|---|
Particle Size | 1.6-1.8mm |
Moisture Content | ≤1% |
Surface Area | 100-110 M2/g |
Pore Volume | 0.6-0.8 Cm3/g |
Bulk Density | 0.6-0.65 G/cm3 |
---|---|
Mgo Content | ≤0.05% |
Thermal Stability | Up To 1200℃ |
Moisture Content | ≤1% |
Particle Size | 1.6-1.8mm |
Mgo Content | ≤0.05% |
---|---|
Crystalline Phase | Q-Al2O3 |
Fe2O3 Content | ≤0.02% |
Moisture Content | ≤1% |
Particle Size | 1.6-1.8mm |